SABIC沙伯基础创新Lexan PC 243R中英文物性表资料
|
SABIC Innovative Plastics Lexan® 243R PC
The property table is provided by www.plas-cn.com, welcome to download, reprint please indicate the source!
|
|
|
Material Notes:
|
LEXAN 243R is a medium viscosity multi purpose UV stabilized grade and contains release agent to ensure easy processing. This grade is UL94-V2 at 0.8 mm approved.
|
|
Physical Properties物理性质
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Density密度
|
1.20 g/cc
|
0.0434 lb/in³
|
ISO 1183
|
|
Moisture Absorption at Equilibrium吸湿平衡
|
0.15 %
|
0.15 %
|
23°C / 50% RH; ISO 62
|
|
Water Absorption at Saturation吸水率
|
0.35 %
@Temperature 23.0 °C |
0.35 %
@Temperature 73.4 °F |
ISO 62
|
|
Linear Mold Shrinkage, Flow线性收缩率/流动
|
0.0050 - 0.0070 cm/cm
|
0.0050 - 0.0070 in/in
|
on tensile bar; SABIC Method
|
|
Melt Flow熔体流动速率
|
12 g/10 min
@Load 1.20 kg, Temperature 300 °C |
12 g/10 min
@Load 2.65 lb, Temperature 572 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133
|
|
Mechanical Properties力学性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Hardness,硬度 H358/30
|
95.0 MPa
|
13800 psi
|
ISO 2039-1
|
|
Tensile Strength at Break断裂拉伸强度
|
70.0 MPa
|
10200 psi
|
50 mm/min; ISO 527
|
|
Tensile Strength, Yield屈服拉伸强度
|
63.0 MPa
|
9140 psi
|
50 mm/min; ISO 527
|
|
Elongation at Break断裂伸长率
|
110 %
|
110 %
|
50 mm/min; ISO 527
|
|
Elongation at Yield屈服伸长率
|
6.0 %
|
6.0 %
|
50 mm/min; ISO 527
|
|
Tensile Modulus拉伸模量
|
2.35 GPa
|
341 ksi
|
1 mm/min; ISO 527
|
|
Flexural Yield Strength弯曲屈服强度
|
90.0 MPa
|
13100 psi
|
2 mm/min; ISO 178
|
|
Flexural Modulus弯曲弹性模量
|
2.30 GPa
|
334 ksi
|
2 mm/min; ISO 178
|
|
Izod Impact, Notched悬臂梁缺口冲击强度 (ISO)
|
12.0 kJ/m²
@Temperature -30.0 °C |
5.71 ft-lb/in²
@Temperature -22.0 °F |
80*10*3; ISO 180/1A
|
|
70.0 kJ/m²
@Temperature 23.0 °C |
33.3 ft-lb/in²
@Temperature 73.4 °F |
80*10*3; ISO 180/1A
|
|
|
Izod Impact, Unnotched悬臂梁无缺口冲击强度 (ISO)
|
NB
@Temperature 23.0 °C |
NB
@Temperature 73.4 °F |
80*10*3; ISO 180/1U
|
|
NB
@Temperature -30.0 °C |
NB
@Temperature -22.0 °F |
80*10*3; ISO 180/1U
|
|
|
Charpy Impact Unnotched夏比缺口试样冲击
|
NB
@Temperature 23.0 °C |
NB
@Temperature 73.4 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU
|
|
NB
@Temperature -30.0 °C |
NB
@Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU
|
|
|
Charpy Impact, Notched夏比缺口冲击
|
1.40 J/cm²
@Temperature -30.0 °C |
6.66 ft-lb/in²
@Temperature -22.0 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
|
|
3.50 J/cm²
@Temperature 23.0 °C |
16.7 ft-lb/in²
@Temperature 73.4 °F |
ISO 179/2C
|
|
|
7.30 J/cm²
@Temperature 23.0 °C |
34.7 ft-lb/in²
@Temperature 73.4 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
|
|
|
Taber Abrasion, mg/1000 Cycles周期泰伯磨耗
|
10
@Load 1.00 kg |
10
@Load 2.20 lb |
CS-17; SABIC Method
|
|
Electrical Properties电性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Volume Resistivity体积电阻率
|
>= 1.00e+15 ohm-cm
|
>= 1.00e+15 ohm-cm
|
IEC 60093
|
|
Surface Resistance表面电阻
|
>= 1.00e+15 ohm
|
>= 1.00e+15 ohm
|
ROA; IEC 60093
|
|
Dielectric Constant介电常数
|
2.7
@Frequency 1.00e+6 Hz |
2.7
@Frequency 1.00e+6 Hz |
IEC 60250
|
|
2.7
@Frequency 50.0 - 60.0 Hz |
2.7
@Frequency 50.0 - 60.0 Hz |
IEC 60250
|
|
|
Dielectric Strength介电强度
|
15.0 kV/mm
@Thickness 1.00 mm |
381 kV/in
@Thickness 0.0394 in |
short time; IEC 60243-1
|
|
17.0 kV/mm
@Thickness 3.20 mm |
432 kV/in
@Thickness 0.126 in |
in oil; IEC 60243-1
|
|
|
Dissipation Factor耗散因数
|
0.0010
@Frequency 50.0 - 60.0 Hz |
0.0010
@Frequency 50.0 - 60.0 Hz |
IEC 60250
|
|
0.010
@Frequency 1.00e+6 Hz |
0.010
@Frequency 1.00e+6 Hz |
IEC 60250
|
|
|
Thermal Properties热性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
CTE, linear, Parallel to Flow线性热膨胀系数
|
70.0 µm/m-°C
@Temperature 23.0 - 80.0 °C |
38.9 µin/in-°F
@Temperature 73.4 - 176 °F |
ISO 11359-2
|
|
Thermal Conductivity导热系数
|
0.200 W/m-K
|
1.39 BTU-in/hr-ft²-°F
|
ISO 8302
|
|
Deflection Temperature at热变形温度 0.46 MPa (66 psi)
|
136 °C
|
277 °F
|
Edgew 120*10*4 sp=100mm; ISO 75/Be
|
|
Deflection Temperature at热变形温度 1.8 MPa (264 psi)
|
125 °C
|
257 °F
|
Edgew 120*10*4 sp=100mm; ISO 75/Ae
|
|
Vicat Softening Point维卡软化点
|
141 °C
|
286 °F
|
Rate B/50; ISO 306
|
|
142 °C
|
288 °F
|
Rate B/120; ISO 306
|
|
|
153 °C
|
307 °F
|
Rate A/50; ISO 306
|
|
|
UL RTI, Electrical相对温度指数
|
130 °C
|
266 °F
|
UL 746B
|
|
UL RTI, Mechanical with Impact机械冲击热指数
|
125 °C
|
257 °F
|
UL 746B
|
|
UL RTI, Mechanical without Impact无机械冲击热指数
|
125 °C
|
257 °F
|
UL 746B
|
|
Flammability, UL94阻燃等级
|
V-2
@Thickness 0.750 mm |
V-2
@Thickness 0.0295 in |
UL 94
|
|
V-0
@Thickness 6.00 mm |
V-0
@Thickness 0.236 in |
UL 94
|
|
|
Oxygen Index氧指数
|
25 %
|
25 %
|
LOI; ISO 4589
|
|
Glow Wire Test灼热丝测试
|
850 °C
@Thickness 1.00 mm |
1560 °F
@Thickness 0.0394 in |
Glow Wire Flammability Index; IEC 60695-2-12
|
|
Optical Properties光学性质
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Refractive Index折射率
|
1.586
|
1.586
|
ISO 489
|
|
Haze雾度
|
<= 0.80 %
@Thickness 2.54 mm |
<= 0.80 %
@Thickness 0.100 in |
ASTM D 1003
|
|
Transmission, Visible透光率
|
88 - 90 %
@Thickness 2.54 mm |
88 - 90 %
@Thickness 0.100 in |
ASTM D 1003
|
昊恩塑胶贸易有限公司为您提供详细的 沙特-SABIC LEXAN PC 243R 物性表参数。
想了解更多的与沙特-SABIC LEXAN PC 243R相关的物性参数，请点击 沙特-SABIC Lexan PC 产品列表。
如果您对我们的沙特-SABIC LEXAN PC 243R有任何疑问，想咨询沙特-SABIC LEXAN PC 243R价格，或是想获取沙特-SABIC LEXAN PC 243R物性表datasheet、物质安全资料证书MSDS、RoHS检验报告、REACH环保证明、FDA证明、UL证书及出厂证明COA报告等，请联系我们。
东莞市昊恩塑胶贸易有限公司：专业从事工程塑胶原料--主要代理销售：(1)：沙伯基础创新塑料(SABIC) ; (2)：美国杜邦(DuPont) ; (3)：比利时-索尔维(solvay) ; (4)：瑞士埃坶斯(ems) ; (5) : 德国巴斯夫(BASF);(6)：德国科思创Covestro) ; (7)：日本帝人(TEIJIN ) ; (8) : 日本旭化成(AsahiKASEI); (9) : 日本宝理(Polyplastics);(10)：英国威格斯 (Victrex )
东莞市昊恩塑胶贸易有限公司不仅是专业的是沙特-SABIC LEXAN PC 243R原料供应商，亦注重技术支持及全方位的解决方案，提供从材料鉴定、模具设计、成型加工等系列帮助，亦可为客户量身定制各特殊性能的材料，帮助客户提高产品竟争力。服务热线：13798909890。
大家都在找
电 话：13798909890 传 真：0769-87128563
网 址：http://www.hao-en.com/ 邮箱：dai@hao-en.com
地 址：东莞市樟木头镇百果洞社区塑胶原料市场第三期商铺A61号
东莞市昊恩塑胶贸易有限公司 版权所有
电 话：13798909890 传 真：0769-87128563
网 址：http://www.hao-en.com/ 邮箱：dai@hao-en.com
东莞市樟木头镇百果洞社区塑胶原料市场第三期商铺A61号 粤ICP备17076707号 百度统计
昊恩塑胶公司专业从事塑胶材料、Lexan pc 工程塑料、Delrin塑胶原料、sabic的牌号的相关产品值得客户信赖的品牌供应商。
扫描二维码
加个人微信